Stainless Steel Plates 201 Discription
Steel 201 Plates does not harden with heat treatment but can be work hardened to high tensile strengths. 201 Stainless Steel plates are widely used in petrochemical industry, nuclear power, water conservancy projects and so on.
Grade 201 Stainless Steel Coils can be formed using all commonly employed forming methods and pressures similar to that of 300 series stainless steels. This Perforated 201 Steel Plates is non-magnetic in the annealed condition, but becomes magnetic when cold worked. Perforated 201 Steel Sheets is also non-hardenable by thermal treatment, but may be cold worked to high tensile strengths. Buy 201 Stainless Steel Plates at affordable price from us.
Specifications : ASTM A240 / ASME SA240
Standard : JIS, AISI, ASTM, GB, DIN, EN
Range : 1000/1219/1500/2000mm,etc
Conventional common size : 4 inch X 8 inch ,10 inch x 5 inch
Thickness : 0.2 mm to 20mm
Form : Coils, Foils, Rolls, Plain Sheet, Shim Sheet, Perforated Sheet, Chequered Plate
Hardness : Soft, Hard, Half Hard, Quarter Hard, Spring Hard etc.
Grades : SS 201 UNS S20100
201 Stainless Steel Plates Chemical Composition
|SS 201||0.020 max||2 max||1.00 max||0.040 max||0.030 max||19.00 – 23.00||4.00 – 5.00||23.00 – 28.00||1.00 – 2.00|
Mechanical Properties of SS 201 Plates
|Density||Melting Point||Tensile Strength||Yield Strength (0.2%Offset)||Elongation|
|7.95 g/cm3||1350 °C (2460 °F)||Psi – 71000 , MPa – 490||Psi – 32000 , MPa – 220||35%|
Equivalent Grades of SS 201 Plates
|SS 201||1.4372||S20100||SUS 201||904S13||STS 317J5||Z2 NCDU 25-20||X1NiCrMoCu25-20-5|